Termékek cink (5)

In order to be able to benefit from the excellent strength values of carbon steels in a heavily corrosive environment – in comparison with expensive stainless steels – Zinc Lamella Coating can be used. Our Zinc Lamella Coating generates the so-called cathodic protection. The more ignoble zinc “sacrifices” itself to protect the base material. Steel can be protected in this way. The layer thickness is between 10 μm and 25 μm, for specific requirements thicker layers are possible. For metric threated parts it is necessary to meet the tolerances according to ISO 965, to avoid the screw thread‘s agglutination and to keep the friction coefficients accordingly adjustable. In contrast to paints, where the danger infiltration is given, this phenomenon is prevented through the „sacrificing“ impact of zinc. In salt spray tests zinc lamella coatings achieve better results than typical galvanic zinc plating, which often only reaches 96 h to 200 h in salt spraying tests (usually according...

"The zinc-nickel process has developed in recent years into a process providing one of the most efficient coatings in surface refinement, and is primarily used where high corrosion resistance at a high temperature load is required. Zinc-nickel alloys with 12-16% nickel content are very temperature-resistant, the higher level of hardness compared to the normal zinc coatings is also a very important property, since the risk of damage is lower. The process is related to the conventional alkaline zinc method, but has excellent durability even without post-treatment. This process is suitable for both barrel and rack goods."

Druckguss, Druckgussformen, Druckgusswerkzeuge, Druckgussteile, Druckgussteile aus zink und zinklegeirungen, Druckgussteile aus Zinkgelgierungen, Druckguss mit Zink, Druckguss Teile, Druckgussteile aus Magnesium, Magnesiumdruckguss, Magnesium druckguss, Magnesium Druckgussteile, aluminium druckguss, aluminium druckgussteile, aluminiumdruckguss, zinkdruckguss, zink druckguss, zinkdruckgussteile, zink druckgussteile, zink druckgießen, magnesium druckgießen, aluminium druckgießen. deutsche Qualität, deutsche Kommunikation, chinesischer Preis, chinesische Geschwindigkeit, bester Service = Runbond Mould

"In phosphating, a phosphorus-containing crystal coating is applied to steel parts and galvanised steel parts by a chemical surface process. There are various phosphate processes, e.g., zinc phosphate, zinc calcium phosphate, iron phosphate. The coating thickness is adjustable for special customer requirements. Beim Phosphatieren steht die Verformbarkeit und die Bildung eines Haftgrundes im Vordergrund. During phosphating processes, the formability and the formation of an adhesive primer is of primary importance. The coating weight is usually in the range of 1 to 15g/m². Phosphatisations are especially resistant to lubricants such as oils or greases, and therefore well-suited to many technical applications. . Phosphate coatings are usually further coated. This involves: Oiling, soaping, lubricant coating, vulcanising and painting."

Druckguss, Druckgussformen, Druckgusswerkzeuge, Druckgussteile, Druckgussteile aus zink und zinklegeirungen, Druckgussteile aus Zinkgelgierungen, Druckguss mit Zink, Druckguss Teile, Druckgussteile aus Magnesium, Magnesiumdruckguss, Magnesium druckguss, Magnesium Druckgussteile, aluminium druckguss, aluminium druckgussteile, aluminiumdruckguss, zinkdruckguss, zink druckguss, zinkdruckgussteile, zink druckgussteile, zink druckgießen, magnesium druckgießen, aluminium druckgießen chinesischer Preis, chinesische Geschwindigkeit, bester Service = Runbond Mould